| COMMERCIAL NAME |
Ultramid
A3EG6 |
| MANUFACTURER/SUPPLIER |
BASF AG |
| FILLER OR COPOLYMER |
Glass fiber 30% |
| SPECIAL FEATURES |
Exc str,stiff,high temp-perform,
&dimensional stability |
| USES |
Mechanical/Electric pts |
| RATINGS |
UL |
PROPERTIES English Metric
Processing Methods |
Injection |
| Processing Temp |
544ºF
284ºC |
| Linear Mold Shrinkage
in/in |
0.0025 |
| Melting Point |
500ºF
260ºC |
| Density lb/ft3
g/cm3 |
84.8 1.36 |
| Tensile Str, Yield lb/in2 kg/cm2 |
2.64×104
1860 |
| Tensile Str,Break
lb/in2
kg/cm2 |
|
| Elongation,Break |
3% |
| Tensile Modulus lb/in2
kg/cm2 |
|
| Flexurals Str, Yield
lb/in2
kg/cm2 |
3.76×104
2650 |
| Flexural Modulus lb/in2
kg/cm2 |
1.21×106
8.5×104 |
| Compressive Str
lb/in2 kg/cm2 |
|
| Izod,Notched, R.T.ft lb/in kg cm/cm |
2.11
11.5 |
| Hardness(Test) |
R121 |
| Linear Therm Expan
in/in °F
cm/cm °C |
1.11×10-5
2.0×10-5 |
| Continuous Svc Temp |
|
| Defl Temp, 264lb/in2 |
482ºF
250ºC |
| Defl Temp, 66 lb/in2 |
482ºF
250ºC |
| Volume Resistivity
Ohm cm |
1.00×1015 |
| Dielectric Strength V/10-3in
V/mm |
2295
9.00×104 |
| Dielectric Constant,106Hz |
3.5 |
| Dissipation Factor,106Hz |
0.014 |
| Water Absorb,24 hr |
0.80% |
| Notes |
|